Product Quality and Specifications Portland Cement/Clinker
UNITED STATES STANDARD ASTM C 150 BRITISH STANDARD BS 12/1996
RUSSIAN STANDARD GOST 1017885 SABS CERTIFIED CONTINGENTS AVAILABLE AT ADDITIONAL COST.
GOST AND BIS CERTIFICATION AVAILABLE UPON REQUEST.
ACCORDING TO BRITISH STANDARDS 12/1996, ASTM C-150 SPECIFICATIONS OF ORDINARY PORTLAND CEMENT GRADE 42.5 N/R CHEMICAL COMPOSITION.
- SILICON DIOXIDE (SIO2) 21
- ALUMINIUM OXIDE (A12O3) 5.3
- FERRIC OXIDE (FE2O3) 3.3
- CALCIUM OXIDE (CAO) 65.6
- MAGNESIUM OXIDE (MGO) 1.1
- SULPHUR TRIOXIDE (SO3) 2.7
- LOSS OF IGNITION (LOI) 0.9
- TRICALCIUM SILICATE (C3S) 60
- DICALCIUM SILICATE (C2S) 15
- TRICALCIUM ALUMINATE (C3A) 8.05
- TRICALCIUM ALUMINO FERRICE (C4AF) 9.76
PHYSICAL AND MECHANICAL PROPERTIES
BLAIN CM2/GR 3.250
AUTOCLAVE EXPANTION 0.02
INITIAL SETTING TIME (VICAT) 105 MINUTES
FINAL SETTING TIME (VICAT) 135 MINUTES
Compressive strength at 3 DAYS 230 KG/CM2
Compressive strength at 7 DAYS 305 KG/CM2
Compressive strength at 28 DAYS 420 KG/CM2
Compressive strength mortar Mpa (N/mm”)
Strength Class: 42,5N
Early Strength: 2 days – 10.00
Strength Class: 42,5R
Early Strength: 2 days – 20.00
Standard 28 days strength: Minimum 42,5. Maximum 62,5